We're in the process of building a cedar-strip row troller. Fiberglassing the transom is the first real experience with the glass. We pre-coated the cedar with epoxy to seal it, then layed out the glass. While wetting out the glass, I can see small slivers of the fiberglass. It does not seem starved, but I'm not sure if it's completely normal.
I tried it again on a scrap piece and it's definetly getting saturated enough, but I still see small slivers of glass in most all areas. This could be normal, but as previously mention, have no experience at what I should be seeing.
The System Three SilverTip is what we are using, slow hardener.

Any advice would greatly be appreciated.